SS861 Silicone Pavement Joint Sealant 590ml Sausages Package

Basic Information
Place of Origin: CHINA
Brand Name: BAIYUN
Model Number: SS861
Minimum Order Quantity: 1000pcs
Packaging Details: 300ml, 500ml.
Delivery Time: 7~14 day
Payment Terms: L/C, T/T
Supply Ability: 400,000pcs /week
Detail Information
Volume: 590 Ml Color: Black, White, Grey
Application: Pavement Shelf Life: 12 Months
Appearance: Paste Composition: One-part, RTV Silicone Sealant, Neutral-curing
Key Words: Silicone Sealant, Pavement
High Light:

Silicone Pavement Joint Sealant

,

590ml Silicone Pavement Joint Sealant


Product Description

SS861 Silicone Pavement Joint Sealant ,590ml Sausages Package. Ready For Use

 

DESCRIPTION

SS861 Silicone Pavement Joint Sealant is cold applied, single component, moisture inducing chemically curing silicone sealant that are based on polymer of polysiloxane structures and are intended for use in weatherproof sealing joints and cracks in Portland concrete highway and airfield pavement. SS861 has high movement ability to meet extremely movement requirement of concrete pavement joints while keeps very low extension stress on weak concrete surface by it slow modulus specialty. Accelerated weathering test showed they could stand strong ultraviolet light and cyclic high-low temperature circumstance of pavement field. Upon being extruded out of package and filled into cleaned joint, the sealant reacts with moisture and in-place silicone rubber durable seal formed.

 

CHARACTERISTICS

  • Ready for use, good extrusion;
  • Neural cure, chemically accommodate to concrete;
  • Chemically form adhesion to concrete substrate, needless primer;
  • High movement ability to withstand extension or shear movement;
  • Low stress on adhesion interface avoid adhesion failure by spalling weak concrete surface;
  • Enough hardness to resist stone debris embed;
  • High rubber recovery to follow cyclic movement;
  • Keep rubber elasticity even temperature low to -40℃, not flow or decompose up to +150℃;
  • Excellent weatherproof performance derived of si-o-si backbone bond witch undestroyed by uv and ozone;
  • Best choice sealant when consider flexible, tough and weather resistant performance.

 

APPLICATIONS

  • Concrete pavement joint sealing to meet high degree movement

 

TYPICAL PROPERTIES

Property Requirement Result Standard
Slump Vertical(mm) ≤3 0 GB/T 13477
horizontal Non Distorted Non Distorted
Extrusion Rate(ml/min) ≥80 487
Tack-Free Time(h) ≤3 1.0
Resilience(%) ≥70 85 JC/T 976
Tensile Modulus(MPa) 23℃ ≤0.4 0.35
-20℃ ≤0.6 /
Bond,Maintained Extension Non Destroyed Non Destroyed
Bond,Variable Temperatures Non Destroyed Non Destroyed
Bond,Water Immersed Non Destroyed Non Destroyed
Bond,Heat Aged Non Destroyed Non Destroyed
Hardness Loss,Heat Aged(HsA) ≤10 3
Heat Aging Loss(%) ≤8 4 GB 16776
Cracks Non Non
Separation Non Non
 

 

APPLICABLE STANDARDS

SS861 Silicone Pavement Joint Sealant meets or exceeds the requirements of the following specifications for one-part sealants.

ASTM Specifications:

  • C920; Type S, Grade NS, Class 50, Use T, A, G, M, O

 

COLORS

SS861 Silicone Pavement Joint Sealant is available in black, gray or other colors on request.

 

PACKAGING

SS861 Silicone Pavement Joint Sealant is available in 10.1 fl. oz. (300 ml) plastic caulking cartridges and 20 fl. oz. (590 ml) foil sausage packs.

 

LIMITATIONS

SS861 Silicone Pavement Joint Sealant should not be used, applied or is not recommended:

  • In structural glazing applications or where the sealant is intended as an adhesive.
  • In areas where abrasion and physical abuse are encountered.
  • In totally confined spaces as the sealant requires atmospheric moisture for cure.
  • On frost-laden or damp surfaces
  • To building materials that bleed oils, plasticizers or solvents – materials such as impregnated wood, oil-based caulks, green or partially vulcanized rubber gaskets or tapes.
  • In below-grade applications
  • On substrates made of polypropylene, polyethylene, polycarbonate and polytetrafluoroethylene.
  • Where movement capability greater than ±12.5% is required.
  • Where painting of the sealant is required, as the paint film may crack and peel
  • For structural adhesion on bare metals or surfaces subject to corrosion (i.e., mill aluminum, bare steel, etc.)
  • To surfaces in contact with food
  • For use underwater or in other applications where the product will be in continuous contact with water.

 

TECHNICAL SERVICE

  • Offer the integral technical data of the products.
  • Adhesion Test:

The products of BaiYun silicone sealant have excellent adhesion to most common building material, as glass,anodized aluminum,ceramic tile,granite,brick,wood, steel and most plastics. But we cannot ensure our sealants are suitable to all materials, as a result of the unceasing appearance of new building materials and the application of new surface treatment technology. In some cases, it is required to have the adhesion test on the substrates. In the laboratory of our factory, we can carry out the adhesion test for clients and give the test report that includes experimental result, recommended products, cleaning methods of the material surface etc.

  • Compatibility Test:

If the accessory like baker, double-sided glue strip can not be compatible with silicone rubber, it may cause silicone rubber to turn colors, even lose adhesion. To avoid these problems, we provide services of compatibility test for clients. Clients can send the accessory to us by mail (or other ways), then we will carry out the compatibility test and give the test report.

  • Staining Test:

We provide services of pollution test for clients. Clients can send the substrates to us by mail (or other ways), then we will carry out the staining test and give the test report.

 

INSTALLATION

Surface Preparation

Sealants may not adhere or maintain long-term adhesion to substrates if the surface is not prepared and cleaned properly before sealant application. Using proper materials and following prescribed surface preparation and cleaning procedures is vital for sealant adhesion. Guangzhou Baiyun Chemical Industry CO., LTD. can provide quality control information and suggestions to user upon request.

 

Materials(Glass, Metals, Plastics, Ceramics, etc.)

  • Clean by using a two-rag wipe technique → wet one rag with solvent and wipe the surface with it, then use the second rag to wipe the wet solvent from the surface BEFORE it evaporates (allowing the solvent to dry on the surface without immediately wiping with a second cloth can negate the cleaning procedure because the contaminants may simply be re-deposited as the solvent dries). In all cases where used, solvents should be wiped dry with a clean, white cloth or other lint-free wiping materials. Change the cleaning rags frequently, as they become dirty. It is easier to see the dirt accumulating on the rag if white rags are used. Do not dip used cleaning rags into the cleaning solvent as this can contaminate the solvent (cleaning with contaminated solvent can result in sealant adhesion issues). Always use clean solvent-resistant containers for solvent use and storage.
  • When cleaning deep, narrow structural glazing cavities, wrap the cleaning cloth around a clean, narrow-blade putty knife. This permits force to be applied to the cleaned surface.
  • Isopropyl Alcohol (IPA) is a commonly-used solvent and has proven useful for most non-porous substrates encountered in architectural construction applications. Xylene and Toluene have also been found useful on many substrates. When handling solvents, refer to manufacturer’s MSDS for information on handling, safety and personal protective equipment.
  • Architectural coatings, paints and plastics should be cleaned with a solvent approved by the manufacturer of the product or which does not harm or alter the finish.
  • Cleaning of surfaces should be done within 1 to 2 hours of when the sealant is to be applied.
  • Difficult or nearly impossible to see on a joint substrate, frost is likely to develop on substrates when temperatures drop near the freezing point. Since frost and moisture will interfere with proper sealant adhesion, it is important to confirm that substrates are dry prior to application of the sealant.

Exterior Insulation and Finish Systems (EIFS)

  • The use of an appropriate silicone primer is required on all EIFS substrates. Consult BAIYUN Technical Services for sealant primer-substrate recommendations.
  • Confirm with the EIFS supplier which finish the sealant should be applied to (i.e., base coat or base coat with EIFS primer).
  • All EIFS surfaces must be clean, dry and sound and in an acceptable condition to receive sealant. Confirm with the EIFS supplier or project architect or consultant, what joint conditions are considered acceptable for sealant installation to proceed. If unacceptable conditions are found, cease installation of sealant until corrections are made.
  • To clean EIFS, lightly abrade the joint surfaces using a synthetic brush or pad and then remove dust and other remaining loose particles with a soft bristle brush or using an oil-free air blow.
  • Cleaning of surfaces should be done within 1 to 2 hours of when the sealant is to be applied.
  • Since EIFS materials can absorb and retain moisture, it is important to confirm that the EIFS materials are dry prior to application of the sealant.

Primers

SS861 Silicone Pavement Joint Sealant will bond to many clean surfaces without the aid of a primer. For difficult-to-bond substrates, the use of a primer or special surface preparation should be evaluated. An evaluation should be made for each specific application/substrate to determine quality of bond. When properly used, primers help assure strong and consistent sealant adhesion to surfaces that may be difficult to bond. Most primers are a blend of organic and inorganic chemicals, resins and solvents. NEVER APPLY PRIMER TO GLASS SURFACES. Obtaining the proper materials, as well as following the prescribed procedures, is vital to ensure the successful use of primers. PRIMER APPLICATION IS NOT A SUBSTITUTE FOR SURFACE PREPARATION. Consult Guangzhou Baiyun Chemical Industry CO., LTD. primer datasheet(s) for specifics and recommendations for use.

 

CAUTION

Primers may contain solvents. When handling solvents, refer to manufacturer’s MSDS for information on handling, safety and personal protective equipment.

 

Masking

The use of masking tape is recommended where appropriate to ensure a neat job and to protect adjoining surfaces from over application of sealant. Masking tape can prevent contact of sealant with adjoining surfaces that otherwise would be permanently marred or damaged by such contact or by cleaning methods required to remove sealant systems. When tooling, use care not to spread the sealant over the face of the substrates adjacent to the joint or masking as the silicone can be extremely difficult to remove on rough or porous substrates. Do not allow masking tape to touch clean surfaces to which the silicone sealant is to adhere (adhesive on masking tape can interfere with adhesion of silicone). Masking tape should be removed immediately after tooling the sealant and before the sealant begins to skin over (tooling time).

 

  • To simplify clean up of excess sealant, use easy to release, pressure sensitive tape to mask adjacent surfaces before applying the structural silicone sealant.
  • Start from the top down and overlap the runs. Tool in direction of over-lap so that masking is not disturbed during tooling.
  • Remove masking immediately after application of silicone or as soon as possible or practical.
  • Drop cloths can be used to cover any surfaces likely to collect excess sealant removed during tooling operations.

 

Sealant Application

  • Apply sealant in a continuous operation, horizontally in one direction and vertically from the bottom to the top of the joint opening, applying a positive pressure adequate to properly fill and seal the joint width.
  • Tool or strike the sealant with a concave tool applying light pressure to spread the material against the back-up material and the joint surfaces to ensure a void-free application.
  • In glazing applications, tool the sealant at the sill so that precipitation and cleaning solutions will not pool.
  • Excess sealant should be cleaned from glass, metal and plastic surfaces while still uncured. On porous surfaces the excess sealant should be allowed to progress through the initial cure or set-up. It should then be removed by abrasion or other mechanical means.
  • Due to the smooth consistency of SS861 Silicone Pavement Joint Sealant, tooling agents such as water, soap, or detergent solutions are not necessary or recommended. Dry tooling is recommended.
  • Sealant application is not recommended when the temperature is below 40°F (4°C) or if frost or moisture is present on the surfaces to be sealed.
  • Application of SS861 Silicone Pavement Joint Sealant is not recommended to surfaces above 122°F (50°C).
  • The cure rate of this product is dependent upon temperature and the availability of atmospheric moisture. Under Standard Conditions (relative humidity of 50 ±5% at an air temperature of 73.4 ±2°F [23 of ±1°C]) this material can attain a cured thickness of 2-3 mm per 24 hours (assuming ample access to atmospheric moisture). As temperature decreases, the cure rate slows down (and vice versa). Low moisture environments will also reduce the cure rate. Near-confined spaces which limit the overall access to atmospheric moisture will cure only from that surface which has access to the atmosphere. Colder temperatures can significantly increase cure times and can open the possibility of sealant irregularities if joint movement occurs while sealant is not fully cured. The following reference provides additional information on Movement-During-Cure of sealant joints: ASTM C1193 – Standard Guide for Use of Joint Sealants; section 12.5.

 

HANDLING AND SAFETY

PRODUCT SAFETY INFORMATION REQUIRED FOR SAFE USE IS NOT INCLUDED IN THIS DOCUMENT. BEFORE HANDLING, READ PRODUCT AND MATERIAL SAFETY DATA SHEETS AND CONTAINER LABELS FOR SAFE USE, PHYSICAL AND HEALTH HAZARD INFORMATION. THE MATERIAL SAFETY DATA SHEET IS AVAILABLE FROM BAIYUN SALES APPLICATION ENGINEER, OR DISTRIBUTOR, OR BY CALLING BAIYUN CUSTOMER SERVICE.

 

USABLE LIFE AND STORAGE

When stored at or below 27ºC (80ºF) in the original unopened containers, this product has a usable life of 9 months from the date of manufacture.

 

PRODUCT SAFETY

Customers considering the use of any of Guangzhou Baiyun Chemical Industry CO., LTD. products should consult the latest Material Safety Data Sheets and labels for product safety information. Customers must evaluate Guangzhou Baiyun Chemical Industry CO., LTD. products and make their own determination as to fitness of use in their particular applications. For Material Safety Data Sheets contact the Guangzhou Baiyun Chemical Industry CO., LTD. sales office nearest you. Customers must ensure that all applicable federal, state, and local requirements have been met before handling any of the products mentioned in the text.

 

LIMITED WARRANTY INFORMATION – PLEASE READ CAREFULLY

The information contained herein is offered in good faith and is believed to be accurate. However, because conditions and methods of use of our products are beyond our control, this information should not be used in substitution for customer’s tests to

ensure that Guangzhou Baiyun Chemical Industry CO., LTD.’s products are safe, effective, and fully satisfactory for the intended end use. Suggestions of use shall not be taken as inducements to infringe any patent.

Guangzhou Baiyun Chemical Industry CO., LTD.’s sole warranty is that the product will meet the Guangzhou Baiyun Chemical Industry CO., LTD. sales specifications in effect at the time of shipment. Your exclusive remedy for breach of such warranty is limited to refund of purchase price or replacement of any product shown to be other than as warranted.

 

GUANGZHOU BAIYUN CHEMICAL INDUSTRY CO., LTD. SPECIFICALLY DISCLAIMS ANY OTHER EXPRESS OR IMPLIED WARRANTY OF FITNESS FOR A PARTICULAR PURPOSE OR MERCHANTABILITY.

GUANGZHOU BAIYUN CHEMICAL INDUSTRY CO., LTD. DISCLAIMS LIABILITY FOR ANY INCIDENTAL OR CONSEQUENTIAL DAMAGES.

 