PPO Solar Panel Silicone Sealant SMG533 Silicone Encapsulant For Solar Cells

Basic Information
Place of Origin: China
Brand Name: BAIYUN
Certification: UL RoHs
Model Number: SMG533
Minimum Order Quantity: Cartridge / Sausage Packaging 1000PCS
Price: Negotiation
Packaging Details: 300 ml
Delivery Time: 7-14days
Payment Terms: L/C, T/T
Supply Ability: Cartridge / Sausage Packaging 1000000PCS/month; Drum Packaging 10000 Kits / month;
Detail Information
Material: Solvent-free Adhesive Package: 24 Pcs Per Box/ 64 Boxes Per Pallet
Volume: 400ml Color: Black White Gray Or Customized Color
High Light:

Solar Panel Silicone Sealant SMG533

,

PPO Solar Panel Silicone Sealant

,

silicone encapsulant for solar cells


Product Description

SMG533 Silicone Sealants Used For Solar Panel Luminum, PPO, TPT/TPE Backsheet Black White Gray Or Customized Color

 

SMG533-S Features

◆ One component, neutral alkoxy curing silicone sealant, fast curing
◆ Easy to use, good aging resistance, water resistance, ozone resistance, UV resistance
◆ It has excellent adhesion to the photovoltaic panel materials, including solar panel aluminum frame, glass, TPT/TPE, etc.
◆ Excellent durability test: Pass the thermal shock test (-40-85℃), damp heat test (85℃/85%RH/1000 h) and other related aging tests. Will not soften or degrade after curing, and always maintain good elasticity
◆ Have complete certification qualifications and passed SGS, UL, TUV certification.

Typical Applications

◆ Used for PV modules frame sealing, junction box adhesion and rail bonding

◆ Solar panel aluminum frame and glass,

◆ TPT/TPE Backsheet

Material Properties

Item Typical Test Standard
Before curing
Appearance White or gray paste Eye-measurement
Density ( g/cm3) 1.4 GB/T 13354-1992
Working time (25℃, 50% RH) 12 GB/T13477.5-20
Extrusion rate (g/min) 52 0.5MPa, 25℃, 3mm
After total curing
Hardness (shore-A) 41 GB/T 531-1999
Tensile Strength (MPa) 2.5 GB/T 528-1998
Elongation break (%) 450 GB/T 528-1998
Shear strength (MPa) 14 GB/T 528-1998
Volume resistivity (Ω.cm) 1.0×1015 GB/T 1962-92
Dielectric strength (KV/mm) 16 GB/T 1408.1-1999
Working temperature (℃) -50-220 /

Noted:All the above data come from 23±2and 50±5%RH curing condations after 7days.

Instructions

◆The surface of substrate must be clean and dry, preferred solvents including isopropanol, acetone, and methyl ethyl ketone.For some special substrates, such as PP and PTEE, needed chemical corrosion or plasma treatment to meet bonding effect.

◆ Match pneumatic dispenser or machine to meet dispensing process.

◆After skin formation, cure continues inward from the surface. In 24 hours (at 25℃and 50% relative humidity). SMG533-S will cure to a depth of about 3.3 mm. The deep-seated part, especially the part that has limit contact with air has longer curing time. Similarly curing time would extend in low-temperature condition.

Packaging & Storage

310 ml/Cartridge; 400ml /Cartridge; 235Kg/55 gallons of pail

Shelf life is 6 month under dry and cool place under 27℃.

Attention

  • Far away from children by storage.
  • In case of contact with shin, wash with water.
  • If accident contact with eyes, flush with plenty of water immediately.
  • Proposed use in a well-ventilated place.

The values in this document are not of all specifications and are subject to change without notice. As the actual situation is very different, it’s hard to guarantee the correctness and applicability of our products in some usage. Users should understand the product before using, and then decide the best way to use it.

PPO Solar Panel Silicone Sealant SMG533 Silicone Encapsulant For Solar Cells 0PPO Solar Panel Silicone Sealant SMG533 Silicone Encapsulant For Solar Cells 1PPO Solar Panel Silicone Sealant SMG533 Silicone Encapsulant For Solar Cells 2

 

Contact Details
Erick Liu

Phone Number : 86-37312985

WhatsApp : +8613711658676