Key Feature: | Low Vapor Transmission Rate | Type: | Two Components |
---|---|---|---|
Material: | 100% RTV Silicone | Color: | Part A: White; Part B: Black; Mixed: Black |
Mixing Ratio: | 9:1~11:1 By Volume | Brand Name: | BAIYUN |
Shelf Life: | 18 Months | ||
Highlight: | Gas Filled IG Insulating Glass Sealant,Triple IG Insulating Glass Sealant,BAIYUN 100 RTV Silicone sealant |
FEATURES
SS616 belongs to RTV-2. The curing speed can be adjustable, and the deep-seated curing speed is fast, and it is suitable to be used in the factory;
Neutral curing, non-corrosive to metal, coated glass etc;
High modulus and high strength;
Release low-molecular-weight alcohol and no unpleasant odor during curing;
Excellent resistance to weather, UV, ozone, water;
Remains flexible over a temperature range of -58°F(-50°C) to 302°F(150°C);
Good compatibility with other neutral silicone sealants.
COMPOSITION
Two-part, neutral-curing
RTV silicone sealant
APPLICATIONS
As a secondary edge adhesive sealant in insulating glass units
TYPICAL PROPERTIES
Property | Result | Test method |
Base-As Supplied | ||
Color | White | |
Physical Form | Paste | |
Specific Gravity | 1.48g/cm³ | ASTM D1875 |
VOC Content | <130g/L | |
Catalyst-As Supplied | ||
Color | Black | |
Physical Form | Viscous Paste | |
Specific Gravity | 1.01 g/cm³ | ASTM D1875 |
VOC Content | <130g/L | |
As catalyzed | ||
Color | Black | |
Specific Gravity | 1.42g/cm³ | ASTM D1875 |
Tooling Time(23°C/73°F, 50% RH) | 10-20minutes | |
Snap time(23°C/73°F, 50% RH) | 20-70mim | |
Flow, Sag or Slump | <0.1mm | ASTM C639 |
Mix Ratio(By volume) | A:B = 9-11:1 | |
Recommend Mix Ratio(By volume) | A:B=10:1 | |
As cured - After 21 days at 23°C (73°F) and 50% RH | ||
Durometer Hardness, Shore A | 48 | ASTM C661 |
Ultimate Tensile Strength | 0.9MPa | ASTM C 1135 |
Ultimate Elongation | 130% | ASTM C 1135 |
Water Vapor Permeability | 15.1.0g/m2/24h | EN1279 |
Specifications:Typical property data values should not be used as specifications. Assistance with specifications are available by contacting Guangzhou Baiyun Chemical Industry CO., LTD. |
DESCRIPTION
BAIYUN SS616 Insulating Glass Sealant is a neutral curing silicone sealant with high modulus and high strength, purposely designed for glazing insulating glass. It has the advantage of low air permeability. SS616 Insulating Glass Sealant works with two-component mixing equipmentand the two components react quickly after mingled in scale, then cures into elastomer
SPECIFICATIONS
SS616 Insulating Glass Sealant meets or exceeds the requirements of the following specifications for two-part sealants.
EN1279-4
HOW TO USE
BAIYUN SS616 Insulating Glass Sealant, when used in non structural applications, must be reviewed by BAIYUN technical service specialists.
Complete design and installation guidelines are contained in the BAIYUN Technical Manual when using this product.
COLORS
A: White; B: Black; After Mixed: Black.
PACKAGING
Part A: Base
Part B: Catalyst
BAIYUN SS616 base and BAIYUN SS616 Catalyst are available separately:
Base: BAIYUN SS616 Base is available in 52 US gallon drum, containing ~47.6 US gallons (180 L) with a polyethylene bag liner.
Catalyst: BAIYUN SS616 Catalyst is available in a 5.3-US gallon pail, containing ~5.0 US gallons (19 L)
LIMITATIONS
BAIYUN SS616 Insulating Glass Sealant should not be used, applied or recommended:
In structural glazing applications.
To building materials that bleed oils, plasticizers or solvents – materials such as impregnated wood, oil-based caulks, green or partially vulcanized rubber gaskets or tapes
When surface temperatures below 4ºC (39.2ºF) or exceed 40ºC (104ºF)
Where painting of the sealant is required, as the paint film may crack and peel
In below-grade applications
For use as an interior penetration fire stop sealing system
In horizontal floor joints where abrasion and physical abuse are likely to be encountered
To frost-laden or damp surfaces
For structural adhesion on bare metals or surfaces subject to corrosion (i.e., mill aluminum, bare steel, etc.)
For contact with strong acids or bases
To surfaces in contact with food
For continuous immersion in water
For water immersion applications.
Do not apply acid-curing (Acetoxy) silicone sealants to this product as this may cause loss of adhesion of SS616 Insulating Glass Sealant to glassor other substrates used in the system
HANDLING AND SAFETY
PRODUCT SAFETY INFORMATION REQUIRED FOR SAFE USE IS NOT INCLUDED IN THIS DOCUMENT. BEFORE HANDLING, READ PRODUCT AND MATERIAL SAFETY DATA SHEETS AND CONTAINER LABELS FOR SAFE USE, PHYSICAL AND HEALTH HAZARD INFORMATION. THE MATERIAL SAFETY DATA SHEET IS AVAILABLE FROM BAIYUN SALES APPLICATION ENGINEER, OR DISTRIBUTOR, OR BY CALLING BAIYUN CUSTOMER SERVICE.
USABLE LIFE AND STORAGE
When stored at or below 27ºC (80ºF) in the original unopened containers, BAIYUN Catalyst and Base of SS616 Insulating Glass Sealant has a usable life of 18 months from the date of manufacture.
HEALTH AND ENVIRONMENT INFORMATION
For information and advice regarding transportation, handling, storage and disposal of chemical products, users should refer to the actual Material Safety Data Sheets containing physical, ecological toxicological and other safety-related data.
LIMITED WARRANTY INFORMATION – PLEASE READ CAREFULLY
The information contained herein is offered in good faith and is believed to be accurate. However, because conditions and methods of using our products are beyond our control, this information should not be used in substitution for customer’s tests to
ensure that the products of Guangzhou Baiyun Chemical Industry CO., LTD are safe, effective, and fully satisfactory for the intended end use. Suggestions of use shall not be taken as inducements to infringe any patent.
The warranty of Guangzhou Baiyun Chemical Industry CO., LTD. is that the product will meet the Guangzhou Baiyun Chemical Industry CO., LTD. sales specifications in effect at the time of shipment. Your exclusive remedy for breach of such warranty is limited to refund of purchasing price or replacement of any product shown to be other than as warranted.